MOLY

Industrial EP grease for extreme loads

Available formats :

Safety Data Sheet
Technical data sheet Safety data sheet moly-2 Safety data sheet moly-1 Safety data sheet moly-0 Safety data sheet moly-32-0 Safety data sheet moly-32-2

Instructions for use

Use MOLY, always ensuring that you follow the equipment manufacturer's recommendations.

Technical Data

Warning

MOLY is not recommended for bearings operating at speeds above 1200 RPM.

When changing greases, make sure to validate the compatibility of the greases in question (consult PROLAB's grease compatibility chart).

Available formats

435 g, 450 g, 17 kg, 55 kg, 180 kg

Product number(s)

#294: MOLY-0 #291: MOLY-1 #293: MOLY-2 #271: MOLY-32-0 #266: MOLY-32-2

Technical specifications
Characteristics ASTM Test Typical Values
MOLY-2 		Typical Values
MOLY-1 		Typical Values
MOLY-0
Appearance/texture   Dark grey, creamy Dark grey, creamy Dark grey, creamy
Molybdenum Disulfide   ≥5.0 wt% ≥5.0 wt%

≥5.0 wt%
N.L.G.I. Grade   2 1 0
Viscosity at 40oC D445 324 cSt 36.9 cSt 42.8 cSt
Viscosity at 100oC D445 26 cSt 6.1 cSt 6.7 cSt
Viscosity Index D2270 ≥ 100 111 110
Dropping Point D2265 327°C 300°C 280°C
Oil Separation at 25°C D1742 0% 0.2% 0.2%
Molecule size   avg. 1.5 mic avg. 1.5 mic avg. 1.5 mic
Cone Penetration D217 265-295 310-340 355-385
Consistency 60 strokes D217 285 (1/10mm) 325 (1/10mm) 370 (1/10mm)
Shear Stability 100,000 strokes D217 <3.6% 2.3% 2.0%
Shear Stability 10,000 strokes (50/50 with water) D217 7.9% 7.9% 8.5%
Rolling Stability D1831 n.d. n.d. n.d.
Bearing Leakage Tendency D4290 n.d. 6.0 gr n.d.

Oxidation Resistance (pressure drop)

- 1000 hrs

- 500 hrs

- 100 hrs

 D942

 

13 psi

8.5 psi

3.8 psi

 

9 psi

n.d.

n.d.

 

10 psi

n.d.

n.d.
Bearing Life D3527 n.d. 100 hrs. 180 hrs.
4-ball Wear (75°C, 40 kg, 1200 rpm, 1h) D2266 0.38 mm 0.4 mm 0.42 mm
Load Index D2596 >100 kg 55 kg 55 kg
Weld Load D2596 800 kg 400 kg 400 kg
Timken Load D2509 32 kg 27 kg 25 kg
Rust Resistance D1743 Pass Pass Pass
Water Washout Resistance at 79°C D1264 1% 5% 7.5%
Copper Strip Corrosion D130 1b 1b 1b
Torque at -40°C D4693 n.d. 6.0 Nm 7.0 Nm
Salt Spray Corrosion (1 mil d.f.t.) B117 >300 hrs. >300 hrs. >300 hrs.

Pumpability

23°C (73°F)

-18°C (0°F)

-23°C (-10°F)

-29°C (-20°F)

-34°C (-30°F)

  

 

279 g/min

1 g/min

0 g/min

0 g/min

0 g/min

 

n.d.

40 g/min

14 g/min

7 g/min

2 g/min

 

n.d.

79 g/min

30 g/min

16 g/min

8 g/min

Description

MOLY with ANTIFRICTION TREATMENT is a superior quality extreme pressure grease that outperforms similar greases on the market.

Characteristics and Benefits

MOLY has a unique formulation combining the following elements:

- 5% molybdenum disulfide complex
- Overbased calcium sulfonate complex
- PROLAB's ANTIFRICTION TREATMENT
- High-quality mineral base oil

This exclusive formula makes MOLY a grease with exceptional performance:

- Very adhesive
- Reduces friction
- Protects against rust, corrosion and oxidation
- Offers exceptional resistance to load, shock and impact
- Offers exceptional resistance to water and washout
- Superior mechanical stability

MOLY's excellent properties help to extend lubrication intervals and save on maintenance costs. Available in three N.L.G.I. grades, MOLY can be used in all seasons.

Types of Applications

MOLY is essential in any business, from the smallest to the largest, regardless of its sector of activity. Highly adhesive, it is recommended for any application where resistance to load and washout is paramount.

It is particularly effective for lubricating pins, joints and slides.